Supported multimetallic catalysts for oxidative dehydrogenation of alkanes

ABSTRACT

A catalyst for oxidative dehydrogenation of alkanes includes a substrate including an oxide; at least one promoter including a transition metal or a main group element of the periodic table; and an oxidation-active transition metal. The catalyst is multimetallic.

STATEMENT OF GOVERNMENT INTEREST

The United States Government claims certain rights in this invention pursuant to Contract No. DE-AC02-06CH11357 between the U.S. Department of Energy and UChicago Argonne, LLC, as operator of Argonne National Laboratory.

FIELD OF INVENTION

The present application relates generally to the field of multimetallic catalysts. In particular, the invention relates to a multimetallic catalyst for oxidative dehydrogenation of alkanes to olefins (alkenes) or diolefins (dienes), a method of synthesizing a multimetallic catalyst for oxidative dehydrogenation of alkanes to olefins (alkenes) or diolefins (dienes), and a method of performing oxidative dehydrogenation of alkanes to olefins (alkenes) or diolefins (dienes) in the presence of a multimetallic catalyst.

BACKGROUND

This section is intended to provide a background or context to the invention recited in the claims. The description herein may include concepts that could be pursued, but are not necessarily ones that have been previously conceived or pursued. Therefore, unless otherwise indicated herein, what is described in this section is not prior art to the description and claims in this application and is not admitted to be prior art by inclusion in this section.

Practical and efficient catalyst technologies for alkane oxidative dehydrogenation (ODH) to value-added olefin products is a rapidly developing area in alkane conversion since the product is an important intermediate for polymers and commodity chemicals production.

Supported transition metal catalysts for oxidative dehydrogenation of alkanes to olefins (alkenes) or diolefins (dienes) deactivate due to facile agglomeration of the active sites during catalysis. Active site agglomeration not only leads to deactivation, but also results in pronounced changes in catalytic selectivity. For example, highly dispersed or isolated manganese oxide sites are more selective for alkane oxidative dehydrogenation, while the corresponding manganese oxide crystallites are good combustion catalysts, producing CO₂ as the main oxidation product. It is then crucial to stabilize site-isolated and/or highly dispersed manganese oxide oligomers on catalyst support surfaces under reaction conditions to suppress hydrocarbon deep oxidation (combustion) and maintain catalyst activity to the higher value olefin products, thereby increasing the efficiency of ODH catalysts.

Relative to direct, non-oxidative dehydrogenation of alkanes, catalytic ODH routes are thermodynamically more favored for the conversion of alkanes to the corresponding alkenes. Site-isolated mid-transition metal oxides (e.g., Mn, Cr) have been shown active and selective for this transformation; however, most of the known ODH catalysts suffer from aggressive deactivation due to active site sintering to form bulk phases (e.g., Mn₂O₃) that are more selective to combustion products (e.g., carbon oxides). A need exists for strategies for active site stabilization under ODH.

There remains no consensus strategy for stabilizing Mn- and Cr-based ODH sites as these metals are largely used as promoters for other redox-active cations (e.g., molybdenum). In most studies and reports on bulk manganese-oxide-based catalysts report ODH activities, however, stability issues remain unresolved. Site-isolation is key in tuning the selectivity of ODH catalytic sites. Most catalyst synthesis strategies reported in the prior art involving mid-transition metal ODH catalysts give a distribution of sites with varying reactivities, hence, impacting the overall reaction selectivity and efficiency.

SUMMARY

Additional features, advantages, and embodiments of the present disclosure may be set forth from consideration of the following detailed description, drawings, and claims. Moreover, it is to be understood that both the foregoing summary of the present disclosure and the following detailed description are exemplary and intended to provide further explanation without further limiting the scope of the present disclosure claimed.

In some embodiments, a catalyst for oxidative dehydrogenation of alkanes includes a substrate including an oxide; at least one promoter including a transition metal or a main group element of the periodic table; and an oxidation-active transition metal. The catalyst is multimetallic.

In some aspects of the catalyst, the oxidation-active transition metal comprises manganese, nickel or vanadium.

In some aspects of the catalyst, the substrate is selected from the group consisting of SiO₂, Al₂O₃, TiO₂, and ZrO₂.

In some aspects of the catalyst, the at least one promoter comprises a Lewis acidic and redox-active promoter.

In some aspects of the catalyst, the at least one promoter comprises an oxide layer of the transition metal or the main group element of the periodic table having a general formula of MO_(x), where M is the transition metal or the main group metal of the periodic table.

In some aspects of the catalyst, the at least one promoter is selected from the group consisting of Zn, Fe, Ga, Cr, Zr, Ni, and V.

In some aspects of the catalyst, the catalyst is doped with an element selected from the Group I elements of the periodic table, the Group II elements of the periodic table, or the main group elements of the periodic table.

In some embodiments, a method of producing an alkene includes providing an alkane; and performing oxidative dehydrogenation on the alkane in the presence of an oxidant (e.g., air or CO₂) and a catalyst to yield an alkene. The catalyst includes a substrate including an oxide; at least one promoter including a transition metal or a main group element of the periodic table; and an oxidation-active transition metal. The catalyst is multimetallic. The alkane and the oxidant are may be present in a 1:1 ratio

In some embodiments, a method of synthesizing a catalyst for oxidative dehydrogenation of alkanes includes providing a substrate includes an oxide; reacting the substrate with at least one promoter to form an intermediary; and reacting the intermediary with an oxidation-active transition metal to form the catalyst. The at least one promoter includes a transition metal or a main group element of the periodic table. The catalyst is multimetallic.

In some aspects of the method, the oxidation-active transition metal comprises manganese, nickel or vanadium.

In some aspects of the method, the substrate is selected from the group consisting of SiO₂, Al₂O₃, TiO₂, and ZrO₂.

In some aspects of the method, the at least one promoter comprises a Lewis acidic and redox-active promoter.

In some aspects of the method, the at least one promoter comprises an oxide layer of the transition metal or the main group element of the periodic table having a general formula of MO_(x), where M is the transition metal or the main group metal of the periodic table.

In some aspects of the method, the at least one promoter is selected from the group consisting of Zn, Fe, Ga, Cr, Zr, Ni, and V.

Some aspects of the method further include doping the catalyst with an element selected from the Group I elements of the periodic table, the Group II elements of the periodic table, or the main group elements of the periodic table.

In some aspects of the method, the oxidation-active transition metal is impregnated in a surface of the at least one promoter.

In some aspects of the method, the oxidation-active transitional metal is formed on a surface of the at least one promoter.

In some aspects of the method, the step of reacting the substrate with the at least one promoter and the step of reacting the intermediary with the oxidation-active transition metal are performed simultaneously.

In some aspects of the method, the step of reacting the substrate with the at least one promoter and the step of reacting the intermediary with the oxidation-active transition metal are performed sequentially.

In some aspects of the method, reacting the substrate with the at least one promoter comprises depositing the at least one promoter on a surface of the substrate via atomic layer deposition; and reacting the intermediary with the oxidation-active transition metal comprises depositing the oxidation-active transition metal on a surface of the intermediary via atomic layer deposition.

In some aspects of the method, reacting the substrate with the at least one promoter comprises performing solution-phase organometallic grafting or electrostatic adsorption; and reacting the intermediary with the oxidation-active transition metal comprises performing solution-phase organometallic grafting or electrostatic adsorption.

BRIEF DESCRIPTION OF THE DRAWINGS

The disclosure will become more fully understood from the following detailed description, taken in conjunction with the accompanying figures, in which:

FIG. 1 is a graph illustration the propylene yield of various examples of multimetallic catalysts synthesized in accordance with the embodiments of the invention.

FIG. 2A is a microscopic image of a bare TiO₂ catalyst.

FIG. 2B is a microscopic image of a fresh low Zn/TiO₂ catalyst.

FIG. 2C is a microscopic image of a spent low Zn/TiO₂ catalyst.

FIG. 2D is a microscopic image of a fresh Mn/Zn/TiO₂ catalyst.

FIG. 2E is a microscopic image of a spent Mn/Zn/TiO₂ catalyst.

FIG. 3A is a microscopic image of a bare ZnO₂ catalyst.

FIG. 3B is a microscopic image of a fresh Ni/ZrO₂ catalyst.

FIG. 3C is a microscopic image of a spent Ni/ZrO₂ catalyst.

FIG. 3D is a microscopic image of a fresh Mn/Ni/ZrO₂ catalyst.

FIG. 3E is a microscopic image of a spent Mn/Ni/ZrO₂ catalyst.

DETAILED DESCRIPTION

Before turning to the figures, which illustrate the exemplary embodiments in detail, it should be understood that the present application is not limited to the details or methodology set forth in the description or illustrated in the figures. It should also be understood that the terminology is for the purpose of description only and should not be regarded as limiting.

The present disclosure describes a method of synthesizing a multimetallic catalyst for oxidative dehydrogenation of alkanes to olefins. The alkanes may be, for example, gaseous alkanes. A general synthetic approach to oxidative dehydrogenation of alkanes using the catalysts of the present disclosure is shown below.

In Reaction Scheme I above, catalyst M′/M/E_(x)O_(y) comprises an oxidation-active transition metal, (M′), at least one promoter (M) comprising a transition metal or main group element, and a substrate surface (E_(x)O_(y)). The oxidation-active transition metal (M′) is typically in an oxidized form. In the presence of O₂ (air) and the catalyst M′/M/E_(x)O_(y), the alkane undergoes oxidative dehydrogenation to produce an olefin (alkene). In the example above, although air is described as the oxidant for the oxidative dehydrogenation process, the concepts disclosed herein are not limited in this regard. In other examples, other oxidants (e.g., CO₂ may be used). In the example above, although the alkane is propane and the olefin is propylene (propene), the concepts disclosed herein are not limited in this regard. In other examples, different alkanes (e.g., C2 to C12) may be used to produce different olefins or diolefins. For example, n-butane may undergo oxidative dehydrogenation in the presence of O₂ (air) and the catalyst M′/M/E_(x)O_(y) to produce 1,3-butadiene. Modified oxide supports equipped with transition metal or main group element promoters are employed for tuning the activity, selectivity and stability of the ODH active site.

In one example, a synthetic approach in forming the catalyst of the present disclosure is shown below.

In the Reaction Scheme II above, L and L′ may be a surface oxygen anion or an organic ligand/capping group.

The substrate surface comprises a support material with the general formula of E_(x)O_(y). In some implementations, the support material is selected from an oxide substrate such as zirconia (ZrO₂), titania (TiO₂), silica (SiO₂) or alumina (Al₂O₃), or the like. Further, the substrate may comprise a substrate surface composed of any of the preceding. The substrate surface may be a high-surface-area substrate. The substrate surface may be formed as a membrane, as a particle (e.g. a bead or powder), or as some other structure. The substrate surface may be a porous body. In various embodiments the substrate surface has a surface area, incrementally, of at least 1 m²/g, at least 5 m²/g, at least 10 m²/g, at least 20 m²/g, at least 40 m²/g, at least 60 m²/g, at least 80 m²/g, and/or at least 100 m²/g. In some embodiments, the substrate surface has a surface area, incrementally, of up to about 10000 m²/g, up to 5000 m²/g, up to 1000 m²/g, up to 500 m²/g, up to 250 m²/g, up to 150 m²/g, up to 120 m²/g, up to 100 m²/g, up to 80 m²/g, and/or up to 60 m²/g. In other embodiments, substrate surface may have a surface area of more than 10,000 m²/g or less than 1 m²/g. The supports may be microporous, mesoporous, non-porous or macroporous in various implementations. Particles of the substrate surface may be of any size appropriate for the scale of the structure.

The promoter comprises a transition metal or main group element (M). Promoters significantly suppress coke deposition under harsh reaction conditions (e.g., 200° C. or higher). Moreover, metal oxide promoters improve catalyst stability and in some implementations, are recyclable after multiple-cycle oxidative dehydrogenations. The transition metal may be, in some implementations, a first row transition metal such as zinc or iron. The main group element may be, in some implementations, gallium. In some implementations, the promoter comprises an oxide layer of the transition metal or main group element having the general formula MO_(x), where M is a transition metal or main group metal. Specifically, MO_(x) may include, but is not limited to, TiO₂, ZrO₂, CoO_(x) (where x ranges between 1 and 1.5), ZnO, MnO_(x) (where x ranges from 1 to 3), B₂O₃, Al₂O₃, and Ga₂O₃. The promoter may be a Lewis acidic and redox-active promoter. In some examples, the catalyst may be a trimetallic catalyst including a plurality of promoters. For example, a trimetallic catalyst may include manganese promoted by nickel and zinc.

The promoter has a thickness. For example, the promoters may be installed as a submonolayer, a full monolayer, or as multilayers (e.g., 2 to 20 layers). In one implementation, the promoter does not provide complete coverage of the substrate surface. For example, the promoter may be deposited by a thin film deposition technique to form a partial monolayer atop the substrate surface. In another implementation, a complete monolayer of the promoter is formed. In yet another implementation, the promoter may include at least 2 layers, at least 3 layers, at least 4 layers, at least 5 layers, and/or at least 10 layers. In some implementation, the promoter comprises multiple metals or metal oxides. In other implementations, the promoter consists essentially of a single transition metal, a single main group element, or a single metal oxide.

The catalytic metal (M′) includes a catalytically active material. In particular, M′ is an oxidation-active transition metal including, but not limited to, manganese, nickel, or vanadium. The catalytic metal (M′) is typically installed in an oxidized form, as opposed to an elemental form. In some implementations, the catalytic metal consists essentially of one of manganese, nickel or vanadium. In other implementations, the catalytic metal consists of one of manganese-containing material, nickel-containing material, or vanadium-containing material. The catalytic metal (M′) may be present on a surface of the promoter (M) or impregnated within the promoter (M).

In some implementations, the promoter (M) and the catalytic metal (M′) may be the same transition metal (e.g., in implementations using dimeric sites). In other implementations, the promoter (M) and the catalytic metal (M′) are different transition metals.

Various synthesis methods may be used for depositing the promoter (M) and the catalytic metal (M′). For example, synthesis methods may include thin-film deposition techniques, such as Atomic Layer Deposition (ALD), solution processes (Sol'n) or strong electrostatic adsorption (SEA). In other words, in the catalyst formation steps of Reaction Scheme II, the promoter (M) and the catalytic metal (M′) may be installed or deposited on the substrate surface via (a) gas-phase deposition (e.g., atomic layer deposition (ALD)) at a temperature, for example, from 50 to 400° C., (b) solution-phase organometallic grafting at room temperature, (c) strong electrostatic adsorption, or (d) a combination thereof. In some implementations, one or more of the catalytic metal (M′), the promoter (M) and the substrate surface can be formed by ALD. ALD utilizes alternating exposures between precursors (i.e. in a gaseous form) and a solid surface to deposit materials in a monolayer-by-monolayer fashion. This process can provide uniformity of the coatings in many embodiments, including on nanoporous substrate materials. A catalyst system may be manufactured using a combination of deposition methods. Further, the number of cycles for each deposition, for example, the number of ALD cycles, may be varied. In some implementations, this process also allows good control over the thickness and composition of the coatings. In one embodiment, ALD may be used to deposit both the promoter (M) and the catalytic metal (M′). In another implementation, ALD may be used to deposit the promoter (M) and a solution-phase process may be used to deposit the catalytic metal (M′). In yet another implementation, SEA may be used to deposit the promoter (M) and a solution-phase process may be used to deposit the catalytic metal (M′).

Although Reaction Scheme II illustrates the promoter (M) being installed on the substrate surface prior to the catalytic metal (M′) being installed, in other implementations, Reaction Scheme II may be modified such that the catalytic metal (M′) is installed prior to depositing the promoter (M) or such that the catalytic metal (M′) and the promoter (M) are installed simultaneously. When gas-phase synthesis is used in the catalyst formation, deposition is performed in two steps: one step to deposit the promoter (M) and another step to deposit the catalytic metal (M′). A purge step in the presence of an inert gas may be performed between the two steps. Moreover, one deposition step may be performed at the same or different temperature conditions than the other deposition step. When solution-phase synthesis is used in the catalyst formation, the promoter (M) and the catalytic metal (M′) may be installed sequentially or simultaneously.

In some implementations, the catalysts disclosed herein may be formed as a promoter deposited on the substrate and a catalytic metal deposited on the promoter. In other implementations, the promoter and the catalytic metal may be interchanged by being introduced to the substrate surface simultaneously. In some implementations, the catalytic metal and the promoter may be discrete layers. In further implementations, the catalytic metal and/or the promoter are each a monolayer or sub-monolayer. In some implementations, the catalytic metal and/or the promoter each may include multiple layers. In some implementations, the catalytic metal and/or the promoter each may include at least 2 layers, at least 3 layers, at least 4 layers, at least 5 layers, and/or at least 10 layers. In other implementations, the catalytic metal and/or the promoter are each formed of isolated sites or extended structures such as clusters, islands, particles, or flakes. In a preferred implementation, the catalytic metal and/or the promoter are each formed of isolated sites or small clusters. The catalyst may, in some implementations, be doped/incorporated with Group I or Group II, or main group elements. For example, the catalyst may be doped with alkali elements (e.g., Li, Na, or K), alkaline earth elements (e.g., Mg or Ca), metalloids (e.g., B), or post-transition metals (e.g., Sn).

In conventional oxidative dehydrogenation reaction schemes (i.e., without the catalysts of the present application) to convert an alkane to an olefin, a ratio of the concentration of the alkane to the concentration of O₂ is approximately 2:1 and the reaction is carried out at a temperature less than 400° C. In such conventional oxidative dehydrogenation reaction schemes, about 8% of the propane is converted. The propylene yield is approximately 3.5%. The selectivity to propylene is about 40% at 8% conversion.

In contrast, performing oxidative dehydrogenation using the catalysts of the present application, a ratio of the concentration of the alkane to the concentration of O₂ is approximately 1:1. This ratio allows for a more compact reactor design. Moreover, using the catalysts of the present application, the reaction can be carried out at a higher temperature than the conventional oxidative dehydrogenation reaction schemes, for example, at a temperature up to 500° C. Some of the catalysts tested (described in further detail below), exhibit overall ODH selectivities to propylene as high as 90% at 10 to 15% conversion, and propylene yields of 7 to 15% at 500° C. Table 1 below summarizes the propylene yield at 500° C. for the catalyst formulations of Examples 1-8.

TABLE 1 Propylene Yield (%) Example Catalyst Formulation at 500° C. 1 Mn/Cr/SiO₂ 7.3 2 Mn/Zr/SiO₂ 7.7 3 Mn/Ni/Al₂O₃ 8.0 4 Mn/Ni/TiO₂ 9.8 5 Mn/Ni/SiO₂ 10.8 6 Mn/N/ZrO₂ 12.0 7 Mn/Ni/ZrO₂ 13.0 8 Mn/V/Al₂O₃ 13.1

In Example 1 of Table 1, the Cr may have a specific surface coverage of approximately 10% of a monolayer. In Example 2 of Table 1, the Zr may have a specific surface coverage of approximately 10% of a monolayer. In each of Examples 3 and 4 of Table 1, the Ni may have a specific surface coverage of approximately 23% of a monolayer. In Example 5 of Table 1, the Ni may have a specific surface coverage of approximately 20% of a monolayer. In Example 6 of Table 1, the Ni may have a specific surface coverage of approximately 100% of a monolayer. In Example 7 of Table 1, the Ni may have a specific surface coverage of approximately 50% of a monolayer. In Example 8 of Table 1, the V may have a specific surface coverage of approximately 50% of a monolayer.

As discussed above, most ODH catalysts aggressively deactivate due to site agglomeration and excessive coke deposition. In order to verify the stability of the catalysts, the propylene yield was observed at 500° C. for at least 25 hours. FIG. 1 is a graph illustrating the propylene yield of various catalyst formulations (formed in accordance with the implementations of this application) over time. As seen in FIG. 1, the catalysts exhibit long term stability in that the propylene yield does not approach zero over time.

Moreover, as seen in a comparison of FIGS. 2A-2E and FIGS. 3A-3E, the catalysts according to the implementations of the invention (see FIGS. 2D, 2E, 3D and 3E) did not exhibit evidence of nanoparticles forming. In other words, there was no evidence of site agglomeration or excessive coke deposition in the spent catalysts.

The implementations above describe methods for synthesizing multimetallic catalysts, and methods for performing oxidation dehydrogenation of alkanes with multimetallic catalysts. In particular, the implementations described herein are directed to the synthesis of highly dispersed transition metal catalysts for alkane oxidative dehydrogenation on various solid oxide supports, and provide stability for the active sites of the catalysts under reaction conditions, thereby preventing the formation of bulk manganese oxide sites that compromise process selectivity to the desired product. The methods enforce site-isolation and employ cationic anchoring sites and promoters that enhance the long-term stability of Mn-based or Ni-based active sites. The multimetallic catalysts described herein are configured for the selective dehydrogenation of alkanes to olefins (e.g., propane ODH to propylene).

The construction and arrangements a multimetallic catalyst for oxidative dehydrogenation of alkanes to olefins or diolefins, a method of synthesizing a multimetallic catalyst for oxidative dehydrogenation of alkanes to olefins or diolefins, and a method of performing oxidative dehydrogenation of alkanes to olefins or diolefins in the presence of a multimetallic catalyst, as shown in the various exemplary embodiments, are illustrative only. Although only a few embodiments have been described in detail in this disclosure, many modifications are possible (e.g., variations in sizes, dimensions, structures, shapes and proportions of the various elements, values of parameters, mounting arrangements, use of materials, colors, orientations, image processing and segmentation algorithms, etc.) without materially departing from the novel teachings and advantages of the subject matter described herein. Some elements shown as integrally formed may be constructed of multiple parts or elements, the position of elements may be reversed or otherwise varied, and the nature or number of discrete elements or positions may be altered or varied. The order or sequence of any process, logical algorithm, or method steps may be varied or re-sequenced according to alternative embodiments. Other substitutions, modifications, changes and omissions may also be made in the design, operating conditions and arrangement of the various exemplary embodiments without departing from the scope of the present invention.

As utilized herein, the terms “approximately,” “about,” “substantially”, and similar terms are intended to have a broad meaning in harmony with the common and accepted usage by those of ordinary skill in the art to which the subject matter of this disclosure pertains. It should be understood by those of skill in the art who review this disclosure that these terms are intended to allow a description of certain features described and claimed without restricting the scope of these features to the precise numerical ranges provided. Accordingly, these terms should be interpreted as indicating that insubstantial or inconsequential modifications or alterations of the subject matter described and claimed are considered to be within the scope of the invention as recited in the appended claims.

With respect to the use of substantially any plural and/or singular terms herein, those having skill in the art can translate from the plural to the singular and/or from the singular to the plural as is appropriate to the context and/or application. The various singular/plural permutations may be expressly set forth herein for the sake of clarity. 

What is claimed:
 1. A catalyst for oxidative dehydrogenation of alkanes, the catalyst comprising: a substrate comprising an oxide; at least one promoter comprising a transition metal or a main group element of the periodic table; and an oxidation-active transition metal, wherein the catalyst is multimetallic.
 2. The catalyst of claim 1, wherein the oxidation-active transition metal comprises manganese, nickel or vanadium.
 3. The catalyst of claim 1, wherein the substrate is selected from the group consisting of SiO₂, Al₂O₃, TiO₂, and ZrO₂.
 4. The catalyst of claim 1, wherein the at least one promoter comprises a Lewis acidic and redox-active promoter.
 5. The catalyst of claim 1, wherein the at least one promoter comprises an oxide layer of the transition metal or the main group element of the periodic table having a general formula of MO_(x), where M is the transition metal or the main group metal of the periodic table.
 6. The catalyst of claim 1, wherein the at least one promoter is selected from the group consisting of Zn, Fe, Ga, Cr, Zr, Ni, and V.
 7. The catalyst of claim 1, wherein the catalyst is doped with an element selected from the Group I elements of the periodic table, the Group II elements of the periodic table, or the main group elements of the periodic table.
 8. A method of producing an alkene comprising: providing an alkane; and performing oxidative dehydrogenation on the alkane in the presence of an oxidant and the catalyst of claim 1 to yield an alkene.
 9. The method of claim 8, wherein the alkane and the oxidant are present in a 1:1 ratio.
 10. A method of synthesizing a catalyst for oxidative dehydrogenation of alkanes, the method comprising: providing a substrate comprising an oxide; reacting the substrate with at least one promoter to form an intermediary, the at least one promoter comprising a transition metal or a main group element of the periodic table; and reacting the intermediary with an oxidation-active transition metal to form the catalyst, wherein the catalyst is multimetallic.
 11. The method of claim 10, wherein the oxidation-active transition metal comprises manganese, nickel or vanadium.
 12. The method of claim 10, wherein the substrate is selected from the group consisting of SiO₂, Al₂O₃, TiO₂, and ZrO₂.
 13. The method of claim 10, wherein the at least one promoter comprises a Lewis acidic and redox-active promoter.
 14. The method of claim 10, wherein the at least one promoter comprises an oxide layer of the transition metal or the main group element of the periodic table having a general formula of MO_(x), where M is the transition metal or the main group metal of the periodic table.
 15. The method of claim 10, wherein the at least one promoter is selected from the group consisting of Zn, Fe, Ga, Cr, Zr, Ni, and V.
 16. The method of claim 10, further comprising doping the catalyst with an element selected from the Group I elements of the periodic table, the Group II elements of the periodic table, or the main group elements of the periodic table.
 17. The method of claim 10, wherein the oxidation-active transition metal is impregnated in a surface of the at least one promoter.
 18. The method of claim 10, wherein the oxidation-active transitional metal is formed on a surface of the at least one promoter.
 19. The method of claim 10, wherein: reacting the substrate with the at least one promoter comprises depositing the at least one promoter on a surface of the substrate via atomic layer deposition; and reacting the intermediary with the oxidation-active transition metal comprises depositing the oxidation-active transition metal on a surface of the intermediary via atomic layer deposition.
 20. The method of claim 10, wherein: reacting the substrate with the at least one promoter comprises performing solution-phase organometallic grafting or electrostatic adsorption; and reacting the intermediary with the oxidation-active transition metal comprises performing solution-phase organometallic grafting or electrostatic adsorption. 